Effect of 3 wt% Al Content and Rapid Solidification on the Erosion-corrosion Behavior of 92 wt% Cu and 5 wt% Ni Alloy in Seawater
A. S. Abdulghani, A. M. Badiea & B. G. Mohammed · Chemical Science International Journal · 2016
A 92 wt% Cu and 5wt% Ni alloy containing 3 wt% Al is subjected to a rapid solidification processing (RSP) using a rotating copper wheel (7.95 cm φ x 5.95 cm w) at 1420 r.p.m, which produces a thin specimen of 2 mm thickness. The specimens with dimensions of 10.8×15.02 mm2 are the...