The boards made from wood and secondary fibers appear to be well correlated secondary fiber/wood fiber proportions in terms of the behavior of the sound acoustic properties. However, boards were generally shown better acoustic (sound absorption) properties in high frequencies. Mo...
Open access
Research Article10.9734/JALSI/2017/37063
It was discovered that an increase in the proportion of secondary fibers has a negative impact on strength and thickness swelling (TS) properties of experimental boards. However, the highest MOR value of 20.0 MPa was found for type 1 board (C1) produced with a 90/10 Wood/Seconder...
Open access
Research Article10.9734/ACSJ/2016/27758
It was realized that both boric acid (BA) and secondary fibers (S) from Old Corrugated Container (OCC) negative impact on thickness swelling (TS) properties of boards in water. However, the highest Modulus of Elasticity (MOE) values of both type boards were found at 90/10 Wood/Se...
Open access
Research Article10.9734/ACSJ/2016/27757
It was realized that both boric acid (BA) and secondary fibers (S) from recycled newsprint papers had negative impact on thickness swelling (TS) properties of boards in water. The highest TS value of 48% was observed in both type boards that produced only from 100% secondary fibe...
Open access
Research Article10.9734/ACSJ/2016/27276
The aim of this study was to investigate experimental panels produced from mixture of agriculture wastes with mineral adducts under synthetic adhesive bonding process. In this respect, the effects of the two different mineral loading as reinforced additive (olivine and dolomite)...
Open access
Research Article10.9734/ajocs/2022/v11i119111