This study characterized 1018 steel case-hardened in processed cassava leaves. The microstructures, phases and case depths of treated samples were characterized and the effect of soaking time on case depth was determined. Standard specimens machined from 1018 steel were pack-cyan...
Open access
Research Article10.9734/ACRI/2018/42632
The synthesis of gold nanoparticles was investigated via the laboratory preparation of the precursor from the precipitated gold using sodium cyanide (NaCN) and cyanide solution from cassava. Characterization studies are carried out using TEM and XRD. The synthesis of gold nanopar...
Open access
Research Article10.9734/ACSJ/2016/25749
D. A. Isadare, M. O. Adeoye, A. R. Adetunji, K. M. Oluwasegun & K. J. Akinluwade·Advances in Research·2015
This paper reports the effect of homogenization treatment on T6 tempering of 6063 aluminium alloy. Wrought 6063 aluminium sample was machined into tensile and impact tests specimens. Samples were also cut for hardness and metallographic works. These samples were divided into two...
Open access
Research Article10.9734/AIR/2015/18166
This paper investigates the influence of diffusion annealing on some mechanical properties of 6063 aluminium alloy. Standard tensile and hardness test samples were subjected to diffusion annealing at 570ºC for 2, 2.5, 3 and 3.5 hours respectively prior to T6 tempering, another se...
Open access
Research Article10.9734/BJAST/2014/10446
This study made a comparison between low and high-temperature pack cyaniding. Specific focus includes microstructure, surface hardness and case depth of treated samples. Standard specimens machined from mild steel were pack cyanided at 550°C (low temperature) and 950°C (high temp...
Open access
Research Article10.9734/ACRI/2018/37198